Propriétés mécaniques
Brass has different mechanical properties due to different zinc content. Fig. 7 is a graph showing the change of mechanical properties of brass with different zinc content. For brass, σb and δ increase with the increase of zinc content. For ( plus ) brass, the strength at room temperature increases continuously before the zinc content increases to about 45 percent . If the zinc content is further increased, the R phase with greater brittleness (solid solution based on Cu5Zn8 compound) appears in the alloy structure, and the strength decreases sharply. The room temperature plasticity of ( plus ) brass always decreases with the increase of zinc content. Therefore, the copper-zinc alloy containing more than 45 percent zinc has no practical value.
Le laiton ordinaire est largement utilisé, comme la ceinture de réservoir d'eau, l'alimentation en eau et le tuyau de drainage, la médaille, le tuyau ondulé, le tuyau serpentin, le tuyau de condenseur, le boîtier de coque, divers produits perforés complexes, le matériel, etc. Avec l'augmentation de la teneur en zinc de H63 à H59, ils peuvent bien résister au traitement à chaud et sont principalement utilisés dans diverses parties de machines et d'appareils électriques, de pièces d'estampage et d'instruments de musique.
Afin d'améliorer la résistance à la corrosion, la résistance, la dureté et l'usinabilité du laiton, une petite quantité d'éléments tels que l'étain, l'aluminium, le manganèse, le fer, le silicium, le nickel, le plomb, etc. (généralement 1 % 2 %, quelques-uns jusqu'à 3 % 4 % et quelques-uns jusqu'à 5 %) sont ajoutés à l'alliage cuivre-zinc pour former des alliages ternaires, quaternaires ou même quinaires, ce qui est complexe
Coefficient équivalent zinc
The microstructure of complex brass can be calculated according to the "zinc equivalent coefficient" of elements added in brass. Because a small amount of other alloying elements are added to Cu-Zn alloy, the /( plus ) phase region in Cu-Zn state diagram usually moves to the left or right. Therefore, the microstructure of special brass is usually equivalent to that of ordinary brass with increased or decreased zinc content. For example, the microstructure of Cu-Zn alloy with 1 percent silicon is equivalent to the alloy structure with 10 percent zinc added in Cu-Zn alloy. So the "zinc equivalent" of silicon is 10. The "zinc equivalent coefficient" of silicon is the largest, which makes the /( plus ) phase boundary in Cu-Zn system significantly move to the copper side, that is, the phase region is strongly reduced. The "zinc equivalent coefficient" of nickel is negative, that is, the phase region is enlarged.
La phase - et la phase - en laiton spécial sont des solutions solides multi-éléments complexes, qui ont un grand effet de renforcement, tandis que la phase - et la phase - dans le laiton commun, il y a de simples solutions solides de Cu-Zn, qui ont un faible effet de renforcement. Bien que l'équivalent en zinc soit équivalent, les propriétés de la solution solide à plusieurs composants et de la solution solide binaire simple sont différentes. Par conséquent, une petite quantité de renforcement multi-éléments est un moyen d'améliorer les propriétés de l'alliage.